TECACOMP® TPE TC white 3975V
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2V32Fd_TECACOMPTPETCwhite3975V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | |
| Apparent Density | 0.48 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/10.0 kg) | 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 15.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.40 | % | ISO 294-4 |
| Flow | 0.42 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/50 |
| Tensile Stress | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 13 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Melting Temperature | 160 | °C | DIN 53765 |
| Specific Heat | 1610 | J/kg/°C | DIN EN 821 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 2.0 | W/m/K | DIN EN 821 |
| -- 2 | 8.0 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 70 | °C | |
| short term | 100 | °C | |
| Thermal Diffusivity | DIN EN 821 | ||
| In-plane | 4.00 | cSt | DIN EN 821 |
| Through-plane | 0.800 | cSt | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.9E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 9.2E+12 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 90 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® R200 GF 30 | Ravago Group | Nylon 6 | Ravamid® |
| RapidVac™ VA-1610 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| TOTAL Polypropylene PPH 3462 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Cheng Yu A779 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| Kepital® TS-22 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |