Durethan® BKV 115 H2.0 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2UqenR_DurethanBKV115H20DUS008000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 15% glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.60 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.20 | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.50 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 114 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.1 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5100 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% strain | 155 | MPa | ISO 178/A |
| 23°C | 175 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 5.6 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA 6-HI, GHR, 14-060, GF15 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | ISO 180/1U |
| 23°C | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 214 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 188 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Homopolymer PP710 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| GAPEX® HP RPP20EU98HB | Ferro Corporation | PP Copolymer | GAPEX® HP |
| GAZOLE™ 6430CF | Gharda Chemicals Ltd. | PBI | GAZOLE™ |
| GERMAFORM 9 GK 30 | Kunststoff-Kontor-Hamburg GmbH | Acetal (POM) Copolymer | GERMAFORM |
| Osterlene® PPC-20-NB | Osterman & Company | PP Impact Copolymer | Osterlene® |