Tecoform® PO20 AR10 NL HS
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecoform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2UlfPi_Tecoform-PO20-AR10-NL-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM, 10% aramide fiber reinforced, heat stabilized, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 7.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Hopper Temperature | 30.0 to 50.0 | °C | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 80.0 to 100 | MPa | |
| Back Pressure | Low |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8231G HS BK-106 | BASF Corporation | Nylon 6 | Ultramid® |
| Dynaglide® DW 611 | DeWAL Industries | PTFE | Dynaglide® |
| Elvamide® 8061 | DuPont Performance Polymers | Nylon, Unspecified | Elvamide® |
| LEXAN™ HFD4211 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Lion Idemitsu Composites PPS Y531F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |