Rilsan® CLEAR G 120 Rnew
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2URlOn_Rilsan-CLEAR-G-120-Rnew-61933.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® Clear G 120 Rnew is a high performance transparent polyamide with outstanding chemical resistance and stress cracking resistance. This grade has been designed for injection molding applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 2.8 | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 82 | ||
| Shore D, 15 sec | 80 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1880 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 76.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | > 50 | % | |
| Flexural Modulus | 1840 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| Glass Transition Temperature | 120 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm, 560 nm) | 90.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 29 to 31 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPTON™ 2004 | Kuraray Co., Ltd. | SEPS | SEPTON™ |
| SLOVAMID® 6 GF 30 FRA 3 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Sylvin 86001-75 Clear Yellow 4183 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APICAL 200AF919 | Kaneka Corporation | PI, TS | APICAL |
| DynaStat® 457 | Polymer Dynamix | PE, Unspecified | DynaStat® |