SLOVAMID® 6 FRC 2 218/1M
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2UOgWg_SLOVAMID-6-FRC-2-218-1M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Designed for electrical use. Comes in red / 218 / design. PA 6 injection for reduced flammability, retarded halogen-free flame retardant. Excellent fluidity of the material makes it suitable for the production of complex large-and small stampings. The possibility of using the products have a wall thickness of 0.5 mm. Quality of surface gloss and color types. Note: The product is sensitive to treatment in terms of temperature, cooling time, mold temperature and medium pressure. All these technical characteristics significantly influence the outcome of crystallization of the material and hence the resulting quality characteristics in terms of color and mechanical properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 to 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.87 | % | |
| Flow | 1.2 | % | |
| Water Content | 0.20 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 2350 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 2.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 80 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature (DSC) | 222 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Pressure | 70.0 to 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TufCoat™ 4550 | Lucite International Inc. | Acrylic (PMMA) | TufCoat™ |
| Alathon® H5234 | LyondellBasell Industries | HDPE | Alathon® |
| Electrafil® PA6/6 CF14 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Karina CLEAR PVC COMPOUND 60/206-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polybilt™ Bitumen Modifier 101 | ExxonMobil Chemical | LDPE | Polybilt™ Bitumen Modifier |