ASTALAC™ ABS EPC
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2ULqtg_ASTALAC-ABS-EPC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS EPC is an injection moulding grade offering an optimum balance of easy platability, impact toughness, product rigidity, heat resistance and mouldability. Typical applications in the automotive area include electroplated grilles and rear decor panels, electroplated interior doorhandle and decorative exterior badges. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS EPCUV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 54 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 42.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.20mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Rear Temperature | 225 - 245 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 6.0 | kN/cm² |
| Injection instructions |
|---|
| Injection Pressure: Minimum |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HI LF | RTP Company | PP, Unspecified | RTP |
| ULTEM™ HU1004 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ALTECH® PBT + ASA A 4212/506 GF3MR9 | ALBIS PLASTIC GmbH | PBT+ASA | ALTECH® PBT + ASA |
| EnviroPCABS 5012 | West Michigan Compounding | PC+ABS | EnviroPCABS |
| Monprene® CP-32263 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |