XENOY™ 2230 resin
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2TzHgf_XENOY-2230-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced, opaque, polycarbonate-based polymer alloy. Offers chemical resistance, dimensional stability and mechanical performance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Specific Volume | 0.824 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.60 to 0.90 | % | |
| Across Flow 1 | 0.60 to 0.90 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.14 | % | |
| Equilibrium, 23°C | 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 120 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2240 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 54.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 129 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 121 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 5.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.1E-5 | cm/cm/°C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 5.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.813 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 254 to 277 | °C | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.552 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 HF TFE 20 | RTP Company | PEEK | RTP |
| McCann PP M40CCPP10 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| Sasol Polymers PP HRV100 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Celstran® +PP-GF20-05CN05 Black | Celanese Corporation | PP Copolymer | Celstran® |
| Chiao Fu PA66 MD212STG18 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |