TAROLOX 111 G4
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2To8Gc_TAROLOX-111-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PET glass fibre reinforced 20%, good temperature resistance, very good chemical resistance, very good mechanical, thermal and electrical properties, low moisture absorption, very good dimensional stability. Product must be dried before moulding. Available: all colours, heat stabilized (H), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 to 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 to 0.50 | % | |
| Across Flow | 0.40 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570, ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7800 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 170 | MPa | ISO 178 |
| Break | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 8.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 42 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 230 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 226 | °C | ISO 306/B50, ASTM D1525 3 |
| Ball Pressure Test (245°C) | Pass | VDE 0470 | |
| Melting Temperature | 252 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.00 mm) | 34 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 90.0 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC101 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| MTEGRITY™ PP Impact Copolymer CP700 | M. Holland Company | PP Impact Copolymer | MTEGRITY™ PP Impact Copolymer |
| ADEKA #50 | Adeka Corporation | PUR-Ester | ADEKA |
| Canuck Compounds 800 Series - BK 8-5-8 | Canuck Compounders Inc. | Polyolefin, Unspecified | Canuck Compounds |
| CERTENE™ EDF-224F | Muehlstein | EVA | CERTENE™ |