Reny® F34
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2StUme_Reny-F34.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® F34 is a Polyarylamide (PARA) material filled with 30% whisker. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® F34 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 11.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.65 | % | |
| Water Absorption (Saturation, 23°C) | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 12300 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 33 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 183 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 275 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 285 | °C | |
| Nozzle Temperature | 285 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA E310 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Trexlink™ 6760 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Zythane® 8085D | Alliance Polymers & Services | TPU, Unspecified | Zythane® |
| AMTOPP TA57 | Inteplast Group | PP, Unspecified | AMTOPP |
| Edgetek™ ET3300-8008 FR Black | PolyOne Corporation | PBT | Edgetek™ |