Hostacom G3 N01 102297
| Category: | PP Copolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2SVHZl_Hostacom-G3-N01-102297.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass coupled PP- homopolymer. Low flow, high stiffness and low CLTE. Low creep under load at elevated temperatures. The product is designed for injection molding of structural parts and is available in a black not specified color. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 1.00 | cm³/10min | |
| 230°C/5.0 kg | 3.00 | cm³/10min | |
| Molding Shrinkage | 0.25 to 1.1 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 6000 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 133 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PC/ABS A2200HF-T7 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| AlphaSeal™ 255 H | AlphaGary | TPE | AlphaSeal™ |
| FHR Polypropylene P4C5B-076 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Sylvin 8225-90FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Pujie ACM-03 | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |