LNP™ LUBRICOMP™ LL004 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2SGAr2_LNP-LUBRICOMP-LL004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound LL-4040 Product reorder name: LL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.3 | % | |
| Across Flow : 24 hr | 1.9 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2900 | MPa | ASTM D638 |
| -- | 3070 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 74.8 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2 |
| Break | 69.6 | MPa | ASTM D638 |
| Break | 69.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.8 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2 |
| Break | 23 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2960 | MPa | ASTM D790 |
| -- | 3320 | MPa | ISO 178 |
| Flexural Strength | 118 | MPa | ASTM D790, ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.52 | ||
| vs. Itself - Static | 0.43 | ||
| Wear Factor - Washer | 128 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 91 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 2.80 | J | ASTM D3763 |
| -- | 1.35 | J | ISO 6603-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SXXIC MILKY WHITE | SRF Ltd. | Nylon 6 | TUFNYL® |
| Chiao Fu PA66 MD312G23 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Geon™ Vinyl Flexible C8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Elastron® G G601.A75.B | Elastron USA, Inc. | SEBS | Elastron® G |
| MAJORIS DW360 - 8229 | AD majoris | PP, Unspecified | MAJORIS |