TECHNYL® C 50H2 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2SAOIY_TECHNYL-C-50H2-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNYL® C 50H2 Natural is a unreinforced melamine cyanurate flame retarded polyamide 6. This product is heat stabilised and can be used for injection moulding and extrusion processes. This product is available in natural & black, and in other colours up |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 2000 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield | 80.0 | -- | MPa | ASTM D638 |
| Yield | 75.0 | 50.0 | MPa | ISO 527-2/1A |
| Break | 80.0 | -- | MPa | ASTM D638 |
| Break | 60.0 | 40.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ||||
| Yield | 3.5 | 5.0 | % | ISO 527-2/1A |
| Break | 15 | -- | % | ASTM D638 |
| Break | 25 | 38 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 3500 | -- | MPa | ASTM D790 |
| -- | 3150 | 2000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 115 | -- | MPa | ASTM D790 |
| -- | 200 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 180 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 65 | -- | J/m | ASTM D256 |
| 23°C | 3.5 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (4 Hz) | 3.50 | -- | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.060 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 475 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.380 mm | V-0 | -- | ||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 700 | -- | °C | |
| 1.60 mm | 700 | -- | °C | |
| 3.20 mm | 700 | -- | °C | |
| Oxygen Index | 36 | -- | % | ISO 4589-2 |
| Fire and Smoke F Index | I2/F2 | -- | NF F16-101 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HI | RTP Company | PP, Unspecified | RTP |
| Prime Polypro™ E223U | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Ferro PP TPP40AN74HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| ENFLEX S3015A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Petrothene® GA501026 | LyondellBasell Industries | LLDPE | Petrothene® |