Badamid® PA612 GF30
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2QkGNG_Badamid-PA612-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® PA612 GF30 is a Polyamide 612 (Nylon 612) material filled with 30% glass fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA612 GF30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8300 | 7800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 142 | 128 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 3.3 | % | ISO 527-2/1A/5 |
| Flexural Stress (23°C, 4.00 mm) | 195 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 212 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 196 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 218 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Soarnol® DC3212B | Soarus L.L.C. | EVOH | Soarnol® |
| Thermoset Plastics DC-441 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Trademark PE LLH08925 | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Innoprene 1350N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |
| LNP™ LUBRICOMP™ CL002 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ LUBRICOMP™ |