AKROMID® T1 GF 50 natural (3376)
| Category: | PPA , Polyphthalamide |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2QgstG_AKROMID-T1-GF-50-natural-3376-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® T1 GF 50 natural (3376) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance and light inherent color Applications are parts with tight dimensional tolerances even under high mechanical load. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.62 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 0.90 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 2.4 | -- | % | ISO 178 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 150 to 160 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 170 to 180 | -- | °C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 360 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20000 | 20000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 270 | 255 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 18000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 380 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 90 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 310 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 230 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 313 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R633H | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| NEFTEKHIM PP 1315M (YX37F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Ipethene® 670 | Carmel Olefins Ltd. | LDPE | Ipethene® |
| LNP™ COLORCOMP™ DX98735H compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| LNP™ LUBRICOMP™ SP003 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |