CarmelStat™ CS 1200
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | CarmelStat™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2PcomG_CarmelStat-CS-1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP for corrugated sheets. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.0 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 550 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 86.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 | ohms | ASTM D4496 |
| Volume Resistivity | 1.0E+9 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Volume Resistivity, ASTM D257: 1e6 to 1e9 ohm-cmSurface Resistivity, SEOS/ESD 11.11: 1e6 to 1e9 ohmsStatic Decay Time, MIL-B 81705C: <2 secImpact Resistance, ASTM D5628: 35J |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ IRE1901 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Vi-Chem PVC VDM88-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| NORYL™ NH4030B resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Bergamid™ A70 UF Grey VN-3921 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Celstran® PP-GF20-03 natural | Celanese Corporation | PP Homopolymer | Celstran® |