| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2PO1Ht_Ghaed-SAN-SAN-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: General grade. Characteristic: high flow, high transparency Application: ABS Compounding ,office application,Cups,cosmetic container, Blower fan, pencil case, juicer, &etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 19 to 24 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | > 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 61.8 | MPa | ASTM D638 |
| Flexural Modulus 2(23°C) | > 3040 | MPa | ASTM D790 |
| Flexural Strength 3(23°C) | > 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 4 | > 1.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 96.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 215 to 225 | °C | |
| Processing (Melt) Temp | 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 6.4mm |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 5111-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Tritan™ TXF1021 | Eastman Chemical Company | Copolyester | Tritan™ |
| Hipolyene 8005 DW | Zylog Plastalloys | TPO (POE) | Hipolyene |
| MARPOL® LL6F 801-HSB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| LG ASA LI923P | LG Chem Ltd. | ASA | LG ASA |