LNP™ COLORCOMP™ NX05467 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2OqR8E_LNP-COLORCOMP-NX05467-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP NX05467 is an unfilled Polycarbonate+ABS resin. Added features of this material are: Non-Chlorinated, Non-Brominated Flame Retardant. Also known as: LNP* COLORCOMP* Compound Cycoloy C6200 Product reorder name: NX05467 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.40 to 0.60 | % | |
| Across Flow | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 66.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 87.0 to 91.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 890 | kV/mm | |
| 1.60 mm, in Oil | 640 | kV/mm | |
| 3.20 mm, in Oil | 430 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 60 Hz | 2.80 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 4.0E-3 | ||
| 60 Hz | 4.0E-3 | ||
| 1 MHz | 8.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.700 mm | HB | ||
| 1.20 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 2.10 mm | 5VB | ||
| 3.40 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 221 to 266 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Nozzle Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 243 to 277 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0339G30CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Braskem PP TI4040WT | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| ASTALON™ H2001R | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| INNOPOL® PP CS 2-9523 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| XENOY™ X5300WX resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |