HiFill® PP CO GF20 CC
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2OqLqx_HiFill-PP-CO-GF20-CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PP CO GF20 CC is a Polypropylene Copolymer (PP Copolymer) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 64.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -29°C, 3.18 mm | 53 | J/m | |
| 23°C, 3.18 mm | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 149 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| CLTE - Flow | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 238 to 266 | °C | |
| Middle Temperature | 238 to 266 | °C | |
| Front Temperature | 238 to 266 | °C | |
| Processing (Melt) Temp | 221 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA66 A326 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Adell Polyamide AF-10-667B | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| KEP® 270 | Kumho Polychem Co., Ltd. | EPDM | KEP® |
| LNP™ LUBRICOMP™ RFP48SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Osterlene® LD1019SA | Osterman & Company | LDPE | Osterlene® |