ASTALAC™ ABS 2041
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2O03OB_ASTALAC-ABS-2041.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALAC™ ABS 2041 is a general extrusion packaging grade developed for fast cycle thermoforming processing. It has an excellent balance of rigidity and impact strength and offers high stress crack resistance to a wide range of food stuffs. It is suitable for use in margarine tubs and lids. Underwriters Laboratory Reference E183535-B. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2200 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 89.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 200 - 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Die Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| Top Roll Temperature: 60 to 80°C Middle Roll Temperature: 70 to 90°C Bottom Roll Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V221-80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| ALTECH® PA66 A 1000/501 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Exelene® PS 6800 | Montachem International, Inc. | PS (GPPS) | Exelene® PS |
| LNP™ LUBRICOMP™ WFL34H compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| PLASTRON™ PAX-GF60-02 | Daicel Polymer Ltd. | Nylon, Unspecified | PLASTRON™ |