LNP™ LUBRICOMP™ LL002 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Lh3wz_LNP-LUBRICOMP-LL002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LL002 is a compound based on Polyetheretherketone containing 10% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound LL-4020 Product reorder name: LL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3330 | MPa | ASTM D638 |
| -- | 3280 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 77.0 | MPa | ASTM D638 |
| Yield | 76.0 | MPa | ISO 527-2/5 |
| Break 3 | 79.0 | MPa | ASTM D638 |
| Break | 73.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.3 | % | ASTM D638 |
| Yield | 5.1 | % | ISO 527-2/5 |
| Break 5 | 52 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3070 | MPa | ASTM D790 |
| -- 7 | 3130 | MPa | ISO 178 |
| Flexural Stress | 103 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.40 | ||
| vs. Itself - Static | 0.35 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.100 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 21.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 84 | J/m | ASTM D256 |
| 23°C 8 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 3000 | J/m | ASTM D4812 |
| 23°C 9 | 160 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.40 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 166 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 155 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 149 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 149 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 Special Resin for Badminton | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Sindustris PC GN1001FA | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| TAROMID B 240 NG4 Y2 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| TOTAL Polystyrene Compound 827 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Delrin® Stock Shapes 570 | Ensinger Inc. | Acetal (POM) Homopolymer | Delrin® Stock Shapes |