AKROTEK® PAEK CF 30 TM black (5217)
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2LgQta_AKROTEK-PAEK-CF-30-TM-black-5217-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PAEK CF 30 TM black (5217) is a 30% carbon fibre reinforced polyetherketoneketone with high flexural strength and good sliding properties as well as good tribological properties Applications are mainly elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength and high stiffness in a temperature environment above 150°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.41 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 230 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 23500 | MPa | ISO 178 |
| Flexural Stress 2 | 335 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 1.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 38 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 280 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 205 | °C | ISO 75-2/C |
| Melting Temperature 4 | 340 | °C | DIN EN 11357-1 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G30 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| VITAMIDE® TR36BK6635 | Jackdaw Polymers | Nylon 66/6 | VITAMIDE® |
| AXELERON™ CS K-3364 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| POLYFLAM® RPP 4000 E | A. Schulman Europe | PP Homopolymer | POLYFLAM® |
| Moplen EP545L | LyondellBasell Industries | PP Impact Copolymer | Moplen |