RTP 1300 C AR 35
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2LYXis_RTP-1300-C-AR-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 - 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6550 | MPa | ASTM D638 |
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 5860 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 110 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.125in.: 7-8mil/in.Tensile Elongation, ASTM D-638, 1-1.5%The value listed as flammability, UL 94, was tested in accordance with RTP test standards. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 302 - 343 | °C | |
| Middle Temperature | 302 - 343 | °C | |
| Front Temperature | 302 - 343 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 UV | RTP Company | Acrylic (PMMA) | RTP |
| TOTAL Polystyrene Impact 6351 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| ALTECH® PC C 1000/686 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Hostacom SD068-4C | LyondellBasell Industries | PP, HMS | Hostacom |
| LNP™ LUBRICOMP™ DL0029E compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |