STYRON™ 5050
| Category: | PS (HIPS) , High Impact Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2LLp4k_STYRON-5050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ 5050 is a high-impact polystyrene resin offering a unique balance combining high flow with excellent appearance, good toughness, and high boss strength and stiffness. It is designed for gas-assist injection molding process and paint-free applications. Main Characteristics
Applications
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 13.8 | MPa | |
| Yield, Injection Molded | 20.0 | MPa | |
| Ultimate, Compression Molded | 16.0 | MPa | |
| Ultimate, Injection Molded | 18.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, Compression Molded | 35 | % | |
| Break, Injection Molded | 40 | % | |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 1810 | MPa | |
| Injection Molded | 2010 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 29.6 | MPa | |
| Injection Molded | 37.2 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| Compression Molded | 96 | J/m | |
| Injection Molded | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Annealed | 90.0 | °C | |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.47 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 153A | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| Eltex® P HL001PF | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® P |
| Epoxies, Ect. 60-7114 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| Karina BLACK PVC COMPOUND 860-48/ 1-AY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301-7932 | Lehmann & Voss & Co. | PPS | LUVOCOM® |