Order Products : sales@su-jiao.com
Moplen HP522H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Kvbmz_Moplen-HP522H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP522H is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). The product is particularly suitable for both plain and coextruded structures for metallization. It does not contain any slip or antiblocking agents and it is Calcium Stearate free. BOPP films made of Moplen HP522H are widely used in the food packaging industry. For regulatory information please refer to Moplen HP522H Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 34.0 | MPa | |
| Break, 23°C | 23.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 12 | % | |
| Break | > 500 | % | |
| Flexural Modulus (23°C) | 1450 | MPa | ISO 178 |
| Coefficient of Friction 1(Dynamic) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent (20 µm) | 2900 | MPa | Internal Method |
| Tensile Strength - MD 2(Break, 20 µm) | 250 | MPa | ASTM D882 |
| Tensile Elongation - MD 3(Break, 20 µm) | 90 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 93.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 4(45°) | 91 | Internal Method | |
| Haze 5(50.0 µm) | 0.30 | % | Internal Method |
| Note Message | |
|---|---|
| 1 . | MTM17029E |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | MA17021 |
| 5 . | MA 17031 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1390 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RheTech Polypropylene HP510-01UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| TES J-50/30/RG | Techmer Engineered Solutions | PC | TES |
| Fainplast PVC RKS 317/WM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| LNP™ LUBRILOY™ UA200A compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |