Ebalta GH 760 / GL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2IxXzg_Ebalta-GH-760-GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta GH 760/GL is a two-components epoxy resin, curing at room temperature, castable to 40 mm. The fine non-grinding fillers lead to good surface slip properties and mechanical workability. For this reason ebalta GH 760/GL is especially suitable for metal sheet tools as well as for foundry equipment. Due to its high strength and excellent dimensional accuracy this system is quite versatile. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 86 - 92 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 6750 - 7750 | MPa | ISO 178 |
| Flexural Stress | 90.0 - 110 | MPa | ISO 178 |
| Compressive Stress | 110 - 130 | MPa | ISO 604 |
| Taber Abrasion Resistance (500 Cycles, 500g, CS-17 wheel) | 20.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 7.5 - 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 61.0 - 65.0 | °C | ISO 75-2/B |
| CLTE - Flow (20 to 50°C) | 5.9E-5 | cm/cm/°C | DIN 53752 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 10 |
| Additional Information |
|---|
| Wear jet test : 257 W(V/t) [mm³/min] (internal tests) |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 2.15 - 2.25 | g/cm³ | |
| Viscosity (25°C) | 8.5 - 11 | Pa·s | |
| Curing Time (20°C) | 18 - 24 | hr | |
| Pot Life 1(20°C) | 45 - 55 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E490 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Witcom PA66 6LC-EM-HS | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| ULTZEX™ 3520L | Prime Polymer Co., Ltd. | LLDPE | ULTZEX™ |
| NITRIFLEX N-612 B | NITRIFLEX | NBR | NITRIFLEX |
| InnoPlus LL8420A | PTT Global Chemical Public Company Limited | LLDPE | InnoPlus |