XYLEX™ X2500UV resin
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Ial9V_XYLEXX2500UVresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XENOY X2500UV is a medium viscosity, unfilled, UV stabilized, elastomer modified PC/PET blend with excellent heat and impact performance. ISO1043-label: PC+PET-I. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/1.2 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.50 - 0.80 | % | Internal method |
| Flow : 3.20mm | 0.50 - 0.80 | % | Internal method |
| Transverse flow 2 | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2200 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.0 | MPa | ASTM D638 |
| Yield 4 | 56.0 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/50 |
| Fracture 5 | 55.0 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield | 5.0 | % | ASTM D638, ISO 527-2/50 |
| Yield 6 | 5.0 | % | ASTM D638 |
| Fracture | 100 | % | ASTM D638 |
| Fracture 7 | 80 | % | ASTM D638 |
| Fracture | 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 8 | 2150 | MPa | ASTM D790 |
| -- | 2100 | MPa | ASTM D790 |
| -- 9 | 2150 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 79.0 | MPa | ASTM D790 |
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0mm span 10 | 79.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11 | ISO 179/1eA | ||
| -30°C | 30 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 12(-30°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 200 | J/m | ASTM D256 |
| 0°C | 450 | J/m | ASTM D256 |
| 23°C | 600 | J/m | ASTM D256 |
| -40°C 13 | 15 | kJ/m² | ISO 180/1A |
| -30°C 14 | 25 | kJ/m² | ISO 180/1A |
| 23°C 15 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 16(-30°C) | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 17 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 108 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 18 | 108 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525, ISO 306/B50 11 19 |
| -- | 145 | °C | ISO 306/A50 |
| -- | 136 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 8.7E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.18 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index (2.7 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 250 - 275 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 260 - 275 | °C | |
| Processing (Melt) Temp | 265 - 275 | °C | |
| Mold Temperature | 60 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 50 mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | Type 1, 50mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SG760 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Network Polymers SMMA MS 170 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| NEXUS Reprocessed Nylon 66 G33 RBK | Nexus Resin Group, LLC. | Nylon 66 | NEXUS Reprocessed |
| Geon™ Vinyl Flexible XV3796 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kumho ABS 750SW | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |