Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Trademark Plastics Corporation
Trademark:	Trademark PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2Ggzw1_Trademark-PE-LLH08925.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Applications:

Heavy Duty Sacks

Industrial Liners

Food Packaging

Commercial Packaging

Properties:

Hexene Comonomer

Excellent Processability

Good Toughness

Increased Stiffness

Additives:

Processing Aid

High Slip

High Antiblock

General Information
Additive	High smoothness High caking resistance Processing aid
Features	Low density Rigid, good High caking resistance hexene comonomer Workability, good Good toughness Compliance of Food Exposure
Uses	Packaging Lining Food packaging Heavy packing bag
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a
Processing Method	Blow film

Physical	Nominal Value	Unit	Test Method
Density	0.925	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.80	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
1% secant, MD : 25 µm, blown film	290	MPa	ASTM D882
1% secant, TD : 25 µm, blown film	345	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Broken, 25 µm, blown film	55.2	MPa	ASTM D882
TD : Broken, 25 µm, blown film	34.5	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Broken, 25 µm, blown film	400	%	ASTM D882
TD : Broken, 25 µm, blown film	700	%	ASTM D882
Dart Drop Impact (Blown Film)	130	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	300	g	ASTM D1922
TD : 25 µm, blown film	650	g	ASTM D1922

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.4 µm, Blown Film)	65		ASTM D2457
Haze (25.4 µm, Blown Film)	18	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	204 - 232	°C

Extrusion instructions
Blow-up ratio: 2:1 or higher

Resin Grade	Manufacturer	Category	Trademark
RANPELEN J-550K	Lotte Chemical Corporation	PP Random Copolymer	RANPELEN
Sinvicomp SRP3605A	Teknor Apex Asia Pacific PTE. LTD.	PVC, Rigid	Sinvicomp
Wondel® P PI0	Nanjing Julong Engineering Plastics Co., LTD	PP, Unspecified	Wondel® P
VECTRA® E540i	Celanese Corporation	LCP	VECTRA®
LNP™ THERMOCOMP™ PX92248 compound	SABIC Innovative Plastics	Nylon 6	LNP™ THERMOCOMP™