Osterlene® CIE-9-00
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Osterman & Company |
| Trademark: | Osterlene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Fo7am_Osterlene-CIE-9-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CIE-9-00 is a crystal polystyrene for both injection molding and cap layer co-extrusion. Injection molding applications such as medical and laboratory parts, tumblers and jewel boxes demonstrate the polymers ability to be molded with minimal stresses and fast cycles. Utilizing CIE-9-00 as a cap layer in cups, plates and other consumer disposables takes advantage of this polymers melt rheology. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3030 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 46.2 | MPa | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed) | 96.7 | °C | ASTM D648 |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 GB 20 | RTP Company | PP Homopolymer | RTP |
| DENIBLEND H | Vamp Tech | PC+ABS | DENIBLEND |
| HI-ZEX™ 2110JH | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| LNP™ STAT-KON™ 9X08403C compound | SABIC Innovative Plastics | TP, Unspecified | LNP™ STAT-KON™ |
| Polygen SC76C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |