Marlex® HHM TR-131
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Saudi Polymers Company |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2F0EgR_Marlex-HHM-TR-131.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This high molecular weight, hexene copolymer is tailored for blown film applications that require:
Typical applications for HHM TR-131 include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - Tangent (Compression Molded) | 760 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 21.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 23.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 660 | % | ASTM D882 |
| Dart Drop Impact 3(25 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 30 | g | ASTM D1922 |
| TD : 25 µm, blown film | 350 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 4 | < -75.0 | °C | ASTM D746A |
| Additional Information |
|---|
| The physical properties were determined on compression moulded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 66 cm |
| 4 . | Type I specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® Q121 GR20 | Razin™ Engineering Plastics | PP Homopolymer | Razalen® |
| Formolene® 1103k | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Glastic® 1605 | Bulk Molding Compounds, Inc. | Polyester, TS | Glastic® |
| InvisiSil™ IVS4752 | Momentive Performance Materials Inc. | Silicone | InvisiSil™ |
| Plenco 06343 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |