Generic PARA - Glass Fiber
| Category: | PARA , Polyarylamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2ENn78_Generic-PARA---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PARA - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 - 1.82 | g/cm³ | ASTM D792 |
| 23°C | 1.43 - 1.77 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 3.6 - 20 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 1.85 - 11.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.15 - 0.31 | % | ASTM D955 |
| 23°C | 0.19 - 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.16 - 0.30 | % | ISO 62 |
| Saturated, 23°C | 0.060 - 0.15 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.70 - 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 7580 - 23400 | MPa | ASTM D638 |
| 23°C | 11900 - 24900 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 152 - 281 | MPa | ISO 527-2 |
| 23°C | 141 - 269 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 3.0 | % | ASTM D638 |
| Fracture, 23°C | 1.6 - 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8500 - 21400 | MPa | ASTM D790 |
| 23°C | 11500 - 23500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 203 - 390 | MPa | ASTM D790 |
| 23°C | 280 - 402 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 - 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 12 - 94 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 73 - 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 640 - 970 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 235 - 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 224 - 230 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 9.8E-6 - 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.0E-5 - 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 - 6.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 3.0E+2 - 2.1E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 20 - 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 320 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 798 - 903 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 121 | °C | |
| Drying Time | 1.0 - 12 | hr | |
| Rear Temperature | 255 - 280 | °C | |
| Middle Temperature | 265 - 280 | °C | |
| Front Temperature | 270 - 281 | °C | |
| Nozzle Temperature | 270 - 281 | °C | |
| Processing (Melt) Temp | 265 - 280 | °C | |
| Mold Temperature | 129 - 133 | °C | |
| Injection Pressure | 84.4 - 103 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PARA - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F800E (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Ablefilm ECF564AHF | Henkel Ablestik | Epoxy | Ablefilm |
| Gallonprene® GP520-3504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Ebalta AH 120 / TGS | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Karina GRAY PVC COMPOUND 812-18/52-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |