Order Products : sales@su-jiao.com
TECACOMP® PEEK TRM XG grey 4006
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2E9Xxa_TECACOMPPEEKTRMXGgrey4006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | |
| Apparent Density | 0.69 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (380°C/5.0 kg) | 35 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (380°C/5.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.74 | % | ISO 294-4 |
| Flow | 0.31 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2/50 |
| Tensile Stress | 180 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8000 | MPa | ISO 178 |
| Flexural Stress 2 | 215 | MPa | ISO 178 |
| Compressive Modulus | 3000 | MPa | ISO 604/1 |
| Compressive Stress | 180 | MPa | ISO 604/5 |
| Flexural Strain 3 | 3.5 | % | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature | |||
| long term | 260 | °C | |
| short term | 300 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 335 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 315 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | DIN 53765 |
| Melting Temperature | 343 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 200 to 300°C | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 200 to 300°C | 1.6E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 4 | 0.30 | W/m/K | DIN EN 821 |
| -- 5 | 0.60 | W/m/K | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.2E+13 | ohms | DIN EN 61340 |
| Volume Resistivity | 1.0E+15 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 180 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 360 - 400 | °C | |
| Mold Temperature | 160 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | Through-plane |
| 5 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECATOR™ T15013 | Ensinger Inc. | PAI | TECATOR™ |
| NOVAREX® 7030R | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
| NOVALAC RX®852 | Vyncolit N.V. | Phenolic | NOVALAC |
| ACCUTECH™ HP0334T20L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| MAJORIS PBT 9237 20 M BLACK 8229 | AD majoris | PBT | MAJORIS |