NOVALAC RX®853G is a phenolic (Phenolic) material, which contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. NOVALAC RX®The main features of 853G are: flame retardant/rated flame chemical resistance high strength Creep resistance Good dimensional stability Typical application areas include: Electrical/electronic applications engineering/industrial accessories electrical appliances House Tools

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Ultra high toughness Good dimensional stability Low smoke High strength Antibacterial property Solvent resistance Good creep resistance alkali resistance acid resistance
Uses	Membrane key switch Pump parts Gear Electrical/Electronic Applications Electrical appliances Power/other tools Connector Application in Automobile Field Shell
Forms	Particle
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.78	g/cm³	ASTM D792, ISO 1183
Bulk Factor	3.0		ASTM D1895
Molding Shrinkage
Flow : Molding	0.10	%	ASTM D955
Flow direction	0.10	%	ISO 294-4
Water Absorption
23°C, 24 hr	0.080	%	ASTM D570
23°C, 24 hr	0.060	%	ISO 62

Hardness	Nominal Value	Test Method
Rockwell Hardness
E scale	80	ASTM D785
E scale	90	ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
Fracture	65.0	MPa	ISO 527-2
--	55.2	MPa	ASTM D638
Flexural Modulus
--	15900	MPa	ASTM D790
--	17000	MPa	ISO 178
Flexural Strength
--	103	MPa	ASTM D790
--	100	MPa	ISO 178
Compressive Strength	190	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
--	56	J/m	ASTM D256A
--	3.5	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
1.8 MPa, not annealed	179	°C	ASTM D648
1.8 MPa, not annealed	210	°C	ISO 75-2/A
Linear thermal expansion coefficient			ASTM D696
Flow	2.0E-5	cm/cm/°C	ASTM D696
Lateral	3.9E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.79	W/m/K	ASTM C177
RTI Elec	150	°C	UL 746
RTI Imp	150	°C	UL 746
RTI	150	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength
-- ¹	14	kV/mm	ASTM D149
-- ²	12	kV/mm	ASTM D149
--	14	kV/mm	IEC 60243-1
Arc Resistance	190	sec	ASTM D495

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.18 mm)	V-1		UL 94

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Back Pressure	0.207	MPa

Injection instructions
Plastication: 50rpmInjection Pressure: Set to give 3 to 5 seconds injection timeHold Pressure: 50 to 100% of injection pressureHold Time: 10 sec minimumCure Time, 0.125 in: 30 to 35 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.25%Flexural Strain, ASTM D790: 0.64%DTUL @264psi - Unannealed, ASTM D648, Post Baked: 550°FDielectric Strength, ASTM D149, 60 Hz, Method A, dry: 355 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, dry: 310 V/milCompressive Strength, ISO 604: 200 MPaDielectric Strength, IEC 243, Method A, wet: 14 V/milCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Injection instructions

Plastication: 50rpmInjection Pressure: Set to give 3 to 5 seconds injection timeHold Pressure: 50 to 100% of injection pressureHold Time: 10 sec minimumCure Time, 0.125 in: 30 to 35 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.25%Flexural Strain, ASTM D790: 0.64%DTUL @264psi - Unannealed, ASTM D648, Post Baked: 550°FDielectric Strength, ASTM D149, 60 Hz, Method A, dry: 355 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, dry: 310 V/milCompressive Strength, ISO 604: 200 MPaDielectric Strength, IEC 243, Method A, wet: 14 V/milCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	NOVALAC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2DpwAc_NOVALAC-RX-853G.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 207 B	RTP Company	Nylon 610	RTP
TEKNIFLEX® PXA 1290	Tekni-Films, a div of Tekni-Plex	Film, Copolyester/PCTFE	TEKNIFLEX®
Hylon® N2033STHLUV2	Ravago Manufacturing Americas, LLC	Nylon 6	Hylon®
Karina IVORY PVC COMPOUND -E 907-35/ 1-AY-AC	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LUVOCOM庐 6-8438-1	Lehmann & Voss & Co.	Nylon 12	LUVOCOM®