Ultramid® B3S HP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2DhG2Y_Ultramid-B3S-HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3S HP is a easy flowing, finely crystalline, injection molding PA6 for fast processing. Applications Typical applications include thiwalled technical parts (eg housing, fittings, grips, small parts, anchors and fixing clamps) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 175 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 160 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3400 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 90.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 10 | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 4.0 | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 200 | -- | kJ/m² | |
| 23°C | 250 kJ/m² | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 4.0 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.30 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Varcum 29320 | Durez Corporation | Phenolic | Varcum |
| Cariflex® IR0310 K | Kraton Polymers LLC | IR | Cariflex® |
| FERREX® GPP40CA04NA | Ferro Corporation | PP Homopolymer | FERREX® |
| LEXAN™ XHT3141 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| TORZEN® G3001HR BK34 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |