Lupoy® GN2101FC
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2DgCTq_Lupoy-GN2101FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant, Heat Resistance Application IT/OA, Electric & Electronic Housing and Components |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 76.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3820 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 138 | °C | ASTM D648 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | ||
| 3.00 mm, ALL | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 200 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 330 | °C | |
| Nozzle Temperature | 290 to 330 | °C | |
| Processing (Melt) Temp | 300 to 340 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 907 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Diakon® MH254 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Hanwha Total PP TB53 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| KPOL-LLDPE LLD K-21/927 | KPOL Chem Co. | LLDPE | KPOL-LLDPE |
| Hostacom EP3307 G12771 | LyondellBasell Industries | PP Copolymer | Hostacom |