Infino AR-6508
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2DLUdE_Infino-AR-6508.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino AR-6508 is a Polybutylene Terephthalate + PET (PBT+PET) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 9.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 205 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 140 | MPa | ASTM D638 |
| Yield | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 3 | 14000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength 4 | |||
| -- | 220 | MPa | ASTM D790 |
| -- | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 110 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 88 | J/m | ASTM D256 |
| 23°C 6 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed, 4.00 mm) | 200 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Thickness 4 mm |
| 6 . | Thickness 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ NOTM-PPC | PolyOne Corporation | Tri (n-octyl) Trimellitate | SynPlast™ |
| Adell Polyamide AR-310 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Ad-Tech Epoxy EL-316 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Bergamid™ B70 MI40 NC004 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Hostacom CR 250 F C21451 | LyondellBasell Industries | PP, Unspecified | Hostacom |