Sumitomo Epoxy E 8701A
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2BqmIU_Sumitomo-Epoxy-E-8701A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E 8701A is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability nd good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.01 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.30 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 68.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 19000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 114 | MPa | ASTM D790 |
| Compressive Strength | 235 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, Compression Molded) | > 282 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 19 | kV/mm | |
| -- 3 | 16 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 4.60 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LLDPE UR644 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| TEREZ SAN 2012 G | TER HELL PLASTIC GMBH | SAN | TEREZ SAN |
| TOTAL Polyethylene HDPE 49080 UV | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Karina IVORY PVC COMPOUND 90900-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ FXM121R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |