Petrothene® NA960000
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Bi16S_Petrothene-NA960000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA 960 is a series of resins designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA 960 exhibits good uniformity, ease of processing and good tensile strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(1.91 mm) | 14.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 1.91 mm) | 660 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM E111 | ||
| MD : Blow film | 200 | MPa | ASTM E111 |
| TD : Blow film | 234 | MPa | ASTM E111 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 24.1 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 16.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 200 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 500 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 300 | g | ASTM D1922 |
| TD : 32 µm, blown film | 130 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Additional Information |
|---|
| Film data obtained from film produced in a 3 1/2" (89 mm) blown film line, commercially available 8" (203 mm) die, 350°F (177°C) melt extrusion temperature, 2:1 BUR, 1.25 mil (32 micron) gauge, 0.025" die gap at 150 lb/hr. |
| Note Message | |
|---|---|
| 1 . | Type 4, 510mm/min |
| 2 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michiflex E9287A | API Polymers, Inc. | TPV | Michiflex |
| tefanyl® VR VRGR 343 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| VECTOR® 4213 | Dexco Polymers LP | SIS+SI | VECTOR® |
| Europrene® N 3980 | Versalis S.p.A. | NBR | Europrene® |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |