LNP™ VERTON™ NV006E compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2BaE6e_LNPVERTONNV006Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* VERTON* Compound PCA-F-7006 EM Product reorder name: NV006E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.39 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.52 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.11 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 132 | MPa | ASTM D638 |
| Yield | 150 | MPa | ISO 527-2 |
| Fracture | 130 | MPa | ASTM D638 |
| Fracture | 150 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.6 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2 |
| Fracture | 1.7 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8270 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C 2 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 14.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 144 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 137 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® G3000HR BK34 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Bayflex® 180 RRIM (20% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Braskem PP C7061-01N | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| LNP™ THERMOCOMP™ IF00C compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| Plaslube® POM CO GF10 SL2 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |