Desmopan® DP 9395AU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2AezHg_Desmopan-DP-9395AU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; with special UV stabilizers; very good hydrolysis and microbial resistance; good low-temperature flexibility; Application; Pneumatic hoses; Profiles; Cable sheathings; Injection molded engineering parts |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1150 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 95 | ||
| Shore D, 15 sec | 46 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 52.7 | MPa | |
| 10% Strain, 23°C | 6.50 | MPa | |
| 50% Strain, 23°C | 11.4 | MPa | |
| 100% Strain, 23°C | 13.8 | MPa | |
| 300% Strain, 23°C | 30.0 | MPa | |
| Tensile Strain 4(Break, 23°C) | 440 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 30.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 440 | MPa | |
| 20°C | 104 | MPa | |
| 60°C | 55.0 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5(23°C) | 100 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 22 | % | |
| 70°C, 24 hr | 40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D GB 30 | RTP Company | Nylon 612 | RTP |
| Quadraflex™ ALE-95A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Bayblend® T88 GF-20 | Covestro - Polycarbonates | PC+SAN | Bayblend® |
| CALSIN SE102 | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |
| PETILEN S 39/71 | PETKIM Petrokimya Holding A.S. | PVC, Flexible | PETILEN |