CYCOLOY™ C3650 resin Datasheet,PC+ABS,SABIC Innovative Plastics-SHANGHAI SUSHENG

Message
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according to DIN VDE 0472/815 for cable channels

General Information
Additive	Flame retardancy
Features	Chlorine Free Impact resistance, high Halogen-free Bromine-free Flame retardancy
Uses	Wire and cable applications Shell
Agency Ratings	DIN VDE 0472 part 815
Processing Method	Extrusion blow molding Profile extrusion molding Injection molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--	1.20	g/cm³	ASTM D792
--	1.18	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)	8.5	g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	8.00	cm³/10min	ISO 1133
Molding Shrinkage - Flow (3.20 mm)	0.40 - 0.60	%	Internal method
Water Absorption (Saturation, 23°C)	0.60	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	124		ISO 2039-2
Ball Indentation Hardness (H 358/30)	113	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ¹	2860	MPa	ASTM D638
--	2600	MPa	ISO 527-2/1
Tensile Strength
Yield ²	64.8	MPa	ASTM D638
Yield	55.0	MPa	ISO 527-2/5
Yield	65.0	MPa	ISO 527-2/50
Fracture ³	51.0	MPa	ASTM D638
Fracture	50.0	MPa	ISO 527-2/5
Fracture	55.0	MPa	ISO 527-2/50
Tensile Elongation
Yield ⁴	4.9	%	ASTM D638
Yield	3.0	%	ISO 527-2/5
Yield	4.5	%	ISO 527-2/50
Fracture ⁵	35	%	ASTM D638
Fracture	55	%	ISO 527-2/5
Fracture	> 50	%	ISO 527-2/50
Flexural Modulus
50.0mm span ⁶	2690	MPa	ASTM D790
-- ⁷	2700	MPa	ISO 178
Flexural Stress
--	100	MPa	ISO 178
Yield, 50.0mm span ⁸	101	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ⁹			ISO 179/1eA
-30°C	13	kJ/m²	ISO 179/1eA
23°C	48	kJ/m²	ISO 179/1eA
Notched Izod Impact
23°C	690	J/m	ASTM D256
-30°C ¹⁰	13	kJ/m²	ISO 180/1A
0°C ¹¹	15	kJ/m²	ISO 180/1A
23°C ¹²	45	kJ/m²	ISO 180/1A
Instrumented Dart Impact (23°C, Total Energy)	65.0	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, unannealed, 3.20mm	100	°C	ASTM D648
0.45 MPa, unannealed, 100 mm span ¹³	102	°C	ISO 75-2/Be
1.8 MPa, unannealed, 3.20mm	88.9	°C	ASTM D648
1.8 MPa, unannealed, 100 mm span ¹⁴	91.0	°C	ISO 75-2/Ae
Vicat Softening Temperature
--	110	°C	ASTM D1525, ISO 306/B120 11 ¹⁵
--	108	°C	ISO 306/B50
Linear thermal expansion coefficient
Flow : -40 to 40°C	7.2E-5	cm/cm/°C	ASTM E831
Flow : 23 to 60°C	8.0E-5	cm/cm/°C	ISO 11359-2
Lateral : -40 to 40°C	7.2E-5	cm/cm/°C	ASTM E831
Lateral : 23 to 60°C	8.0E-5	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.20	W/m/K	ISO 8302
RTI Elec	60.0	°C	UL 746
RTI Imp	60.0	°C	UL 746
RTI	60.0	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity	> 1.0E+15	ohms·cm	IEC 60093
Dielectric Strength			IEC 60243-1
0.800mm, in oil	35	kV/mm	IEC 60243-1
1.60mm, in oil	25	kV/mm	IEC 60243-1
3.20mm, in oil	17	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
50 Hz	2.80		IEC 60250
60 Hz	2.80		IEC 60250
1 MHz	2.70		IEC 60250
Dissipation Factor
50 Hz	6.0E-3		ASTM D150
60 Hz	6.0E-3		ASTM D150
50 Hz	4.0E-3		IEC 60250
60 Hz	4.0E-3		IEC 60250
1 MHz	6.0E-3		IEC 60250
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.50 mm	V-0		UL 94
2.49 mm	5VB		UL 94
Oxygen Index	37	%	ISO 4589-2

Extrusion instructions
Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 227 - 249 °C Barrel - Zone 1 Temperature: 204 - 232 °C Barrel - Zone 2 Temperature: 216 - 243 °C Barrel - Zone 3 Temperature: 216 - 243 °C Barrel - Zone 4 Temperature: 221 - 249 °C Die Temperature: 238 - 249 °C Drying Temperature: 79 - 91 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 8 hrs Head - Zone 6 - Top Temperature: 227 - 249 °C Head - Zone 7 - Bottom Temperature: 227 - 249 °C Maximum Moisture Content: 0 - 0.02 % Melt Temperature (Parison): 227 - 249 °C Mold Temperature: 66 - 88 °C Profile Extrusion Parameters: Adapter Temperature: 227 - 271 °C Barrel - Zone 1 Temperature: 204 - 249 °C Barrel - Zone 2 Temperature: 216 - 260 °C Barrel - Zone 3 Temperature: 216 - 260 °C Barrel - Zone 4 Temperature: 227 - 271 °C Calibrator Temperature: 60 - 82 °C Die Temperature: 227 - 271 °C Drying Temperature: 79 - 91 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 8 hrs Melt Temperature: 227 - 271 °C Minimum Moisture Content: 0 - 0.02 %

Extrusion instructions

Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 227 - 249 °C Barrel - Zone 1 Temperature: 204 - 232 °C Barrel - Zone 2 Temperature: 216 - 243 °C Barrel - Zone 3 Temperature: 216 - 243 °C Barrel - Zone 4 Temperature: 221 - 249 °C Die Temperature: 238 - 249 °C Drying Temperature: 79 - 91 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 8 hrs Head - Zone 6 - Top Temperature: 227 - 249 °C Head - Zone 7 - Bottom Temperature: 227 - 249 °C Maximum Moisture Content: 0 - 0.02 % Melt Temperature (Parison): 227 - 249 °C Mold Temperature: 66 - 88 °C Profile Extrusion Parameters: Adapter Temperature: 227 - 271 °C Barrel - Zone 1 Temperature: 204 - 249 °C Barrel - Zone 2 Temperature: 216 - 260 °C Barrel - Zone 3 Temperature: 216 - 260 °C Barrel - Zone 4 Temperature: 227 - 271 °C Calibrator Temperature: 60 - 82 °C Die Temperature: 227 - 271 °C Drying Temperature: 79 - 91 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 8 hrs Melt Temperature: 227 - 271 °C Minimum Moisture Content: 0 - 0.02 %

Note Message
1 .	50 mm/min
2 .	Type 1, 50mm/min
3 .	Type 1, 50mm/min
4 .	Type 1, 50mm/min
5 .	Type 1, 50mm/min
6 .	1.3 mm/min
7 .	2.0 mm/min
8 .	1.3 mm/min
9 .	80104 sp=62mm
10 .	80104
11 .	80104
12 .	80104
13 .	120104 mm
14 .	120104 mm
15 .	标准 B (120°C/h), 载荷2 (50N)

Category:	PC+ABS , Polycarbonate + ABS
Manufacturer:	SABIC Innovative Plastics
Trademark:	CYCOLOY™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	29qpGG_CYCOLOY-C3650-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Caltex PP HG41	GS Caltex	PP, Unspecified	Caltex PP
Fainplast PVC GK 91	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
Dryflex® 400901S	ELASTO	SBS	Dryflex®
LEXAN™ 241S resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
Sarlink® TPE EE-2280B (PRELIMINARY DATA)	Teknor Apex Company	TPE	Sarlink® TPE