3M™ Dyneon™ PTFE TF 1641
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 29KFbN_3M-Dyneon-PTFE-TF-1641.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Free-flowing PTFE for general moulding Features
Typical applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.15 | g/cm³ | ISO 12086 |
| Apparent Density | 0.84 | g/cm³ | ISO 60 |
| Molding Shrinkage | 2.7 | % | Internal Method |
| Average Particle Size | 450 | µm | ISO 13320 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 600 | MPa | ISO 527-2 |
| Deformation Under Load 1(15 MPa) | 17.0 | % | ASTM D621 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (200 µm) | 36.0 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 200 µm) | 430 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | DIN 53752 | ||
| 30 to 100°C | 1.2E-4 | cm/cm/°C | |
| 30 to 200°C | 1.4E-4 | cm/cm/°C | |
| 30 to 260°C | 1.7E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.22 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength (0.200 mm) | 60 | kV/mm | ISO 12086 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PBT-15GF | Polymer Technology and Services, LLC | PBT | PTS |
| Amodel® AFA-6145 V0 Z | Solvay Specialty Polymers | PPA | Amodel® |
| LEXAN™ EXL1112T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Hifax CA1110 G3 1740 | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ THERMOCOMP™ DF002ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |