NEALID XN013C - 8428
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 28e8gW_NEALID-XN013C---8428.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID XN013C - 8428 is a polyamide alloy with detergent additives and low friction intended for injection moulding. APPLICATIONS NEALID XN013C - 8428 has been developed especially for very demanding applications in automotive industry, electrical and appliances parts requiring excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 1.4 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 225 to 245 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 235 to 255 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF13N2441/1 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Vydyne® R513H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| INTEGRATE™ NE542013 | LyondellBasell Industries | Polyolefin, Unspecified | INTEGRATE™ |
| Karina HONEY PVC COMP -E TR 500D22/173 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECHNYL® A 217-1 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |