LNP™ THERMOCOMP™ RC006 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 28dgDg_LNPTHERMOCOMPRC006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RC006 is a compound based on PA6.6 resin containing Carbon Fiber. Added features include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound RC-1006 Product reorder name: RC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | Internal method | ||
| -- | 0.050 - 1.0 | % | Internal method |
| -- 1 | 0.040 - 0.080 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.1 | % | ISO 62 |
| Saturated, 23°C | 4.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 261 | MPa | ISO 527-2/5 |
| Fracture | 250 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 18900 | MPa | ISO 178 |
| Flexural Stress | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | ISO 180/1A |
| -20°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 6 | 260 | °C | ISO 75-2/Be |
| 0.45 MPa, unannealed, 64.0mm span 7 | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 100 mm span 8 | 257 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 9 | 252 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| -- | 4.3E+3 | ohms | IEC 60093 |
| Volume Resistivity | 4.3E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 mm |
| 7 . | 80*10*4 mm |
| 8 . | 120*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 4513 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Nipol® AR 22 | Zeon Corporation | Rubber | Nipol® AR |
| Nypol® PA A3 G30 HL CNZA178 NR466 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DURACON® M90-45LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Hostacom ERC 161N G21259 | LyondellBasell Industries | PP Copolymer | Hostacom |