Hostacom EKC 170N C12470
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 28SWOV_Hostacom-EKC-170N-C12470.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom EKC 170N is a mineral filled polypropylene copolymer, high flow, good stiffness-impact balance, good UV-resistance, low odour, fogging & carbon-emission. The grade has been designed for the moulding large complex parts that requires good dimensional stability. The grade is available in customized colour, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Secant | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 51.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® L L2128 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Vi-Chem PVC VDM93 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TITANLENE® LE4001 | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Cevian®-V VF191 | Daicel Polymer Ltd. | ABS | Cevian®-V |
| EPDM 430 | The Dow Chemical Company | EPDM | EPDM |