LUBLENE GF30 NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBLENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 28NwRy_LUBLENE-GF30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PP first choice natural colour. With glass fibres 30%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 to 1.14 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 to 6000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 70.0 to 80.0 | MPa | |
| Break | 70.0 to 80.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 2.0 to 2.5 | % | |
| Break | 2.0 to 2.5 | % | |
| Flexural Modulus 1 | 4500 to 5500 | MPa | ISO 178 |
| Flexural Stress 2 | 80.0 to 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 to 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 to 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 50 to 60 | J/m | ASTM D256A |
| 23°C 3 | 30 to 40 | kJ/m² | ASTM D256 |
| 23°C | 5.0 to 6.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 5.0 to 6.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 30 to 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 to 155 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 145 to 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 130 to 140 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 155 to 165 | °C | ISO 306/A120 |
| -- | 125 to 135 | °C | ISO 306/B120 |
| Melting Temperature | 165 to 170 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP540R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Thermoset Plastics UR-124 | Thermoset, Lord Chemical Products | PUR, Unspecified | Thermoset Plastics |
| Hylon® N2013L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| LEXAN™ BM5225X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| SABIC® PPcompound 9154 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |