PLEXIGLAS® Film 0F063 is a very high weather resistant and transparent acrylic film for graphic printings and lamination systems. Due to its excellent performance under weathering and UV light exposure, PLEXIGLAS® Film 0F063 does not present color change or yellowing. Therefore it provides high protection of polymeric substrates from degradation caused by UV radiation. It´s very smooth surface leads the film to have a good optical quality surface. Application PLEXIGLAS® Film 0F063 is suitable as top layer for high UV and weathering protection of different polymeric substrates including ones based on Fiber Reinforced Polyester Resin. PLEXIGLAS® Film 0F063 can be used to be printed on as good quality film decoration and then laminated on different polymeric films or sheets. Laminated decoration films based on PLEXIGLAS® are suitable for a wide range of molding processes such as thermoforming, and insert molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | DIN 53479 |
| Surface Tension | 50 | mN/m | DIN 53364 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance - 280 - 380 nm | < 1.0 | % | DIN EN 410 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Accelerated Weathering Resistance - method A, cycle 1, 65% RH 1 | No Visible Change | ISO 4892-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| Yield | 7.0 | % | |
| Break | 21 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 114 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ISO 13468-2 |
| Note Message | |
|---|---|
| 1 . | 8,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraypef® 20030 AP61 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| API PS 650-21 | American Polymers, Inc. | PS (HIPS) | API PS |
| Karina IVORY PVC COMPOUND -E 90850-35/1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND -E 550D48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax TYC 852P E S82786 | LyondellBasell Industries | PP Copolymer | Hifax |