Ultraform® N 2310 P Q600
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 27CUU4_Ultraform-N-2310-P-Q600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultraform N 2310 P Q600 is a general-purpose injection molding POM grade containing special lubricant. Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical properties. Applications Typical applications include spring elements, clips, gears and other applications requiring low friction and wear. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.18 mm | 2.0 | % | |
| Across Flow | 2.1 | % | ISO 294-4 |
| Flow | 2.1 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | 0.80 | % | ASTM D570 |
| Saturation, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 61.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, 23°C) | 10 | % | ASTM D638, ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 30 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1900 | MPa | |
| 1000 hr | 1300 | MPa | |
| Flexural Modulus (23°C) | 2340 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 180 | kJ/m² | |
| 23°C | 200 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 55 | J/m | |
| 23°C | 64 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 154 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 99.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Peak Melting Temperature | 166 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | |||
| -- | 6.0E-5 | cm/cm/°C | ASTM E831 |
| -- | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+12 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | |||
| 1.50 mm | 1.0E+12 | ohms·cm | ASTM D257 |
| -- | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 5.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 3.50 to 7.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCY-5035B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DINALON® A3S25 | Grupo Repol | Nylon 66 | DINALON® |
| GPPC PS-350S | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| Hostalen GD 4755 | LyondellBasell Industries | HDPE | Hostalen |
| Rotuba CAP CP808 (9% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |