Optema™ TC 220 ExCo

Category:	EMA , Ethylene Methyl Acrylate Copolymer Resin
Manufacturer:	ExxonMobil Chemical
Trademark:	Optema™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	25azyy_Optema-TC-220-ExCo.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Optema TC 220 is an ethylene-methyl acrylate copolymer, which can be used to manufacture alloys, mixed ingredients and compounds that require flexibility and elasticity. It is also an excellent grade suitable for coextrusion coating and extrusion into layers requiring good inner adhesion between polyethylene, polypropylene, nylon, polydichloroethylene or other substrates. Processing conditions: Excellent extrusion coating effect can be obtained in the temperature range of 260°C to 300°C (500 °F - 572 °F). It is recommended that the processing temperature should not be higher than 320°C (608 °F). Optema EMA can be processed on traditional extrusion equipment for extrusion coating low density polyethylene. Its wide range of thermal stability makes it suitable for a wide range of processing conditions. The feed pipe of the extruder should be cooled by water to avoid bridging the feed port.

Message

Optema TC 220 is an ethylene-methyl acrylate copolymer, which can be used to manufacture alloys, mixed ingredients and compounds that require flexibility and elasticity. It is also an excellent grade suitable for coextrusion coating and extrusion into layers requiring good inner adhesion between polyethylene, polypropylene, nylon, polydichloroethylene or other substrates. Processing conditions: Excellent extrusion coating effect can be obtained in the temperature range of 260°C to 300°C (500 °F - 572 °F). It is recommended that the processing temperature should not be higher than 320°C (608 °F). Optema EMA can be processed on traditional extrusion equipment for extrusion coating low density polyethylene. Its wide range of thermal stability makes it suitable for a wide range of processing conditions. The feed pipe of the extruder should be cooled by water to avoid bridging the feed port.

General Information
Additive	heat stabilizer

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.0	g/10 min	ASTM D1238
Methyl Acrylate Content	24.0	wt%	ExxonMobil Method

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	43.0	°C	ASTM D1525

Legal statement
有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用

Extrusion instructions
Excellent results are obtained in extrusion coating at 260°C to 300°C (500°F - 572°F) temperature range. Processing temperatures above 320°C (608°F) are not recommended. Optema EMA can be processed on conventional extrusion equipment designed for extrusion coating LDPE. Their broad thermal stability range offer wide processing conditions window. Water cooling of extruder throat is preferred to avoid hopper bridging.

Extrusion instructions

Excellent results are obtained in extrusion coating at 260°C to 300°C (500°F - 572°F) temperature range. Processing temperatures above 320°C (608°F) are not recommended. Optema EMA can be processed on conventional extrusion equipment designed for extrusion coating LDPE. Their broad thermal stability range offer wide processing conditions window. Water cooling of extruder throat is preferred to avoid hopper bridging.

Resin Grade	Manufacturer	Category	Trademark
TOTAL Polyethylene MDPE HT 514	TOTAL Refining & Chemicals	MDPE	TOTAL Polyethylene
HIPLEX® HHM 5502	HIP-PetroHemija	HDPE	HIPLEX®
KumhoSunny PBT/PET HEB4050M	Shanghai KumhoSunny Plastics Co., Ltd.	PBT+PET	KumhoSunny PBT/PET
LNP™ LUBRICOMP™ KI001XXJ compound	SABIC Innovative Plastics	Acetal (POM) Copolymer	LNP™ LUBRICOMP™
TOTAL Polystyrene EPS XLR 5359SE	TOTAL Refining & Chemicals	PS (EPS)	TOTAL Polystyrene