RTP 2000 AG-360
| Category: | PSU Alloy , Polysulfone Alloy |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 25VkNQ_RTP-2000-AG-360.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | % | ASTM D955 |
| Moisture Content | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8960 | MPa | ASTM D638 |
| Tensile Strength | 117 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 7930 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 199 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 343 - 382 | °C | |
| Mold Temperature | 93.3 - 163 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 6620 | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| Quantum Composites QC-8777 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| CALP MRP312 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LNP™ LUBRICOMP™ FL003 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| Lucent PA L6-140 | Lucent Polymers, Inc. | Nylon 66 | Lucent PA |