AGILITY™ 1022 Performance LDPE
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 25DsqY_AGILITY-1022-Performance-LDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY™ 1022 Performance LDPE resin is a high pressure LDPE resin designed to run at faster output rates on blown film lines in LLDPE blends while maintaining optics. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 0.452 | J | |
| Film Puncture Force | 17.8 | N | |
| Film Puncture Resistance | 2.48 | J/cm³ | |
| Film strength | ASTM D882 | ||
| MD | 28.1 | J/cm³ | ASTM D882 |
| TD | 42.2 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 201 | MPa | ASTM D882 |
| 2% secant, MD | 181 | MPa | ASTM D882 |
| 1% secant, TD | 250 | MPa | ASTM D882 |
| 2% secant, TD | 212 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 10.7 | MPa | ASTM D882 |
| TD : Yield | 11.7 | MPa | ASTM D882 |
| MD : Fracture | 23.1 | MPa | ASTM D882 |
| TD : Fracture | 13.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 150 | % | ASTM D882 |
| TD : Fracture | 380 | % | ASTM D882 |
| Dart Drop Impact | 55 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 260 | g | ASTM D1922 |
| TD | 120 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 60 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions for 1 mil monolayer blown film at 100% Die Diameter: 8 in. Screw Type: DSB II Die Gap: 70 mil Output: 12 lb/hr/in. of die circumference Screw Size: 3.5 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 50 rpm Frost Line Height: 39 in. Melt Temperature: 383°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 80A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| SureSpec LD20-020C | Genesis Polymers | LDPE | SureSpec |
| Mylar® S (48 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Nypol® PA A3 G10 UV PRTA011 NR436 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Magnobond 87 | Magnolia Plastics, Inc. | Epoxy | Magnobond |